Material
PTFE filled with Barium Sulphate
pT diagrams
The Klinger pT diagram provides guidelines for determining the suitability of a particular gasket material for a specific application based on the operating temperature and pressure only. Always refer to the chemical resistance of the gasket to the fluid.
1. In area one, the gasket material is normally suitable subject to chemical compatibility.
2. In area two, the gasket materials may be suitable but a technical evaluation is recommended.
3. In area three, do not install the gasket without a technical evaluation.
Technical Data – Typical values for 1.5mm thickness
| Compressibility ASTM F 36 J | 4% |
| Recovery ASTM F 36 J | 40% |
| Stress relaxation DIN 52913 30 MPa, 16 h/150°C |
18MPa |
| Klinger cold/hot compression | |
| 23°C / 50 MPa | 10% |
| 260°C / 50 MPa | 40% |
| Tightness DIN 3535/6 | 0.1 ml/min |
| Tightness DIN 28090-2 | 0.01 mg/s m |
| Thickness/weight increase | |
| HNO3, 100%: 18 h/23°C | 1/2% |
| NaOH, 33%: 72 h/110°C | 1/1%} |
| Density | 3.0g/cm3 |
Dimensions of the standard sheets
Sizes: 1500 x 1500 mm
Thicknesses: 1.0 mm, 1.5 mm, 2.0 mm, 3.0 mm; other thicknesses and sizes on request.
Thickness acc. DIN 28091-1, length ± 50 mm, width ± 50 mm
Function and durability
The performance and service life of KLINGER gaskets depend in large measure on proper storage and fitting, factors beyond the manufacture’s control. We can, however, vouch for the excellent quality of our products. With this in mind, please also observe our installation instructions.