Material
Based on graphite and synthetic fibres. Manufactured using a process which provides the graphite gaskets with totally new, previously unachievable properties.
pT diagram
The Klinger pT diagram provides guidelines for determining the suitability of a particular gasket material for a specific application based on the operating temperature and pressure only. Always refer to the chemical resistance of the gasket to the fluid.
1. In area one, the gasket material is normally suitable subject to chemical compatibility.
2. In area two, the gasket materials may be suitable but a technical evaluation is recommended.
3. In area three, do not install the gasket without a technical evaluation.
Technical Data – Typical values for 1.5mm thickness
| Compressibility ASTM F 36 J | 10% |
| Recovery ASTM F 36 J min. | 60% |
| Stress relaxation DIN 52913 50 MPa, 16 h/300°C |
32MPa |
| Klinger cold/hot compression 50 MPa | |
| thickness decrease at 23°C | 10% |
| thickness decrease at 300°C | 10% |
| Tightness according DIN 3535/6 ml/min | 0,5 |
| Thickness increase ASTM F 146 | |
| water: 5 h/100°C | 5% |
| fuel B: 5 h/23°C | 7% |
| Density | 1,75g/cm3 |
Meet the technical requirements of BS 7531:2006 Grade AX
Dimensions of the standard sheets
Sizes: 1,000 x 1,500 mm, 2,000 x 1,500 mm.
Thicknesses: 0.5 mm, 0.8mm,1.0 mm, 1.5 mm, 2.0 mm, 3.0 mm, other thicknesses on request.
Tolerances: thickness ± 10%, length ± 50 mm, width ± 50 mm
Function and durability
The performance and life of KLINGER gaskets depend in large measure on proper storage and fitting, factors beyond the manufacture’s control. We can, however, vouch for the excellent quality of our products. With this in mind, please also observe our installation instructions